N	Card	Specie	Formula	Upot	Ionic Strength Factor
1.	1175	[1], t-diopside, Mn	(Ca,Mn)(Mg,Mn)[Si2O6]	32418	32
2.	1177	[3], t-diopside	CaMgSi2O6	33136	32
3.	1178	[4], t-diopside, at 24oC	CaMgSi2O6	32466	32
4.	1179	[5], t-diopside, at 400oC	CaMgSi2O6	32320	32
5.	1180	[6], t-diopside, at 700oC	CaMgSi2O6	32224	32
6.	1181	[7], t-diopside, at 850oC	CaMgSi2O6	32179	32
7.	1182	[8], t-diopside, at 1000oC	CaMgSi2O6	32144	32
8.	1183	[9], t-diopside, at 1 atm	CaMgSi2O6	32452	32
9.	1184	[10], t-diopside, at 23.6 kbar	CaMgSi2O6	32670	32
10.	1185	[11], t-diopside, at 35.2 kbar	CaMgSi2O6	32701	32
11.	1186	[12], t-diopside, at 45.5kbar	CaMgSi2O6	32852	32
12.	1187	[13], t-diopside, at 53.0 kbar	CaMgSi2O6	32916	32
13.	1188	[14], t-diopside, at 24oC	CaMgSi2O6	32464	32
14.	1189	[15], t-diopside, at 800oC	CaMgSi2O6	32479	32
15.	1190	[16], t-diopside, at 1000oC	CaMgSi2O6	32479	32
16.	1191	[17], t-diopside, analogue	NaFeGe2O6	33059	33
17.	1192	[18], alpha, t-diopside, analogue	Na2V2O6	37700	38
18.	1196	[22], t-diopside, analogue	Cd2Ge2O6	30694	32
19.	1198	[24], t-diopside, Ni-analogue	CaNiSi2O6	32550	32
20.	1199	[25], t-diopside, Co-analogue	CaCoSi2O6	32345	32
21.	1200	[26], t-diopside, syn, at 1330oC	CaMgSi2O6	32449	32
22.	1201	[27], t-diopside, syn, at 1288oC	CaMg0.8Fe0.2Si2O6	32393	32
23.	1202	[28], t-diopside, syn, at 1222oC	CaMg0.7Fe0.3Si2O6	32372	32
24.	1203	[29], t-diopside, syn, at 1150oC	CaMg0.5Fe0.5Si2O6	32302	32
25.	1204	[30], t-diopside, Fs(75)Wo(25)	(Ca,Fe)2Si2O6	32280	32
26.	1205	[31], t-diopside, Fs(80)Wo(20)	(Ca,Fe)2Si2O6	32331	32
27.	1206	[32], t-diopside, analogue	KInGe2O6	31720	33
28.	1207	[33], t-diopside, In-analogue, at 1770oK + 6 GPa	NaInSi2O6	33215	33
29.	1208	[34], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa	NaIn0.8Sc0.2Si2O6	33247	33
30.	1209	[35], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa	NaIn0.65Sc0.35Si2O6	33279	33
31.	1210	[36], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa	NaIn0.6Sc0.4Si2O6	33288	33
32.	1211	[37], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa	NaIn0.5Sc0.5Si2O6	33315	33
33.	1212	[38], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa	NaIn0.4Sc0.6Si2O6	33327	33
34.	1213	[39], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa	NaIn0.2Sc0.8Si2O6	33368	33
35.	1218	[44], t-diopside, analogue	MgGeO3	15990	16
36.	1226	[52], t-diopside, analogue	(Li,Na)GaSi2O6	34707	33
37.	1227	[53], t-diopside, analogue	(Li,Na)GaSi2O6	34671	33
38.	1228	[54], t-diopside, analogue	(Li,Na)GaSi2O6	34617	33
39.	1229	[55], t-diopside, analogue	(Li,Na)GaSi2O6	34459	33
40.	1230	[56], t-diopside, analogue	(Li,Na)GaSi2O6	34420	33
41.	1231	[57], t-diopside, analogue, at 1770oK+6 GPa	LiGaSi2O6	34537	33
42.	1232	[58], t-diopside, analogue, at 1073oK+1 atm	LiGaSi2O6	34533	33
43.	1233	[59], t-diopside, analogue, at 1123oK+1 atm	LiGaSi2O6	34533	33
44.	1239	[65], t-diopside, at 0 GPa, analogue	FeGeO3	16020	16
45.	1240	[66], t-diopside, at 1.5 GPa, analogue	FeGeO3	16105	16
46.	1241	[67], t-diopside, at 4.5 GPa, analogue	FeGeO3	16248	16
47.	1242	[68], t-diopside, at 7.4 GPa, analogue	FeGeO3	16347	16
48.	1243	[69], t-diopside, at 8.2 GPa, analogue	FeGeO3	16389	16
49.	6221	[77], t-diopside, syn	CaMgSi2O6	32447	32
50.	6222	[78], t-diopside, syn	CaMgSi2O6	32434	32
51.	6223	[79], t-diopside, Fe-analogue	Ca(Mg,Fe)Si2O6	32390	32
52.	6224	[80], t-diopside, Fe-analogue	Ca(Mg,Fe)(Si,Fe)2O6	32393	32
53.	6225	[81], t-diopside, Fe-analogue	Ca(Mg,Fe)(Si,Fe)2O6	32361	32
54.	6226	[82], t-diopside, Fe-analogue	Ca(Mg,Fe)(Si,Fe)2O6	32332	32
55.	6227	[83], t-diopside, Fe-analogue	Ca(Mg,Fe)(Si,Fe)2O6	32273	32
56.	3879	[85], t-diopside, Li-Sc, analogue	LiScSi2O6	33768	33
57.	3880	[86], t-diopside, Ni, analogue	CaNi0.8Mg0.2Si2O6	32528	32
58.	3881	[87], t-diopside, Ni, analogue	CaNi0.5Mg0.5Si2O6	32501	32
59.	3882	[88], t-diopside, Ni, analogue	CaNi0.25Mg0.75Si2O6	32492	32
60.	3883	[89], t-diopside, Ni, analogue	CaNiSi2O6	32542	32
61.	3885	[90], t-diopside, Na, In, analogue	NaInSi2O6	33224	33
62.	3876	[91], t-diopside, Na- Sc- analogue	NaScSi2O6	33409	33
63.	6367	[94], t-diopside, analogue	CaZnSi2O6	32338	32
64.	6368	[95], t-diopside, analogue	CaZnGe2O6	31491	32
65.	6688	[96], t-diopside, analogue, at 25oC	[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6	33002	32
66.	6689	[97], t-diopside, analogue, at 200oC	[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6	32962	32
67.	6690	[98], t-diopside, analogue, at 400oC	[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6	32906	32
68.	6691	[99], t-diopside, analogue, at 620oC	[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6	32839	32
69.	6692	[100], t-diopside, at 10oK	CaMgSi2O6	32503	32
70.	2892	[102], t-diopside, at 1atm	CaMgSi2O6	32465	32
71.	3136	[103], t-diopside, at 4.22GPa	CaMgSi2O6	32831	32
72.	3147	[104], t-diopside, at 8.01GPa	CaMgSi2O6	33128	32
73.	3374	[105], t-diopside, at 10.16GPa	CaMgSi2O6	33281	32
74.	7894	[106], t-diopside, analogue, at 4oK	CoGeO3	16213	16
75.	7895	[107], t-diopside, analogue, at 50oK	CoGeO3	16212	16
76.	7896	[108], t-diopside, analogue, at 298oK	CoGeO3	16193	16
77.	7897	[109], t-diopside, analogue, at 303oK	LiGaSi2O6	34740	33
78.	7898	[110], t-diopside, analogue, at 673oK	LiGaSi2O6	34632	33
79.	7899	[111], t-diopside, analogue, at 1073oK	LiGaSi2O6	34520	33