N/N | x/a | y/b | z/c | B(j) | Occupancy |
---|---|---|---|---|---|
1 | 0.0000 | 0.0000 | 0.0000 | 0.0000 | Sn |
2 | 0.3004 | 0.3110 | 0.0022 | 0.0000 | Ca |
3 | 0.2707 | 0.0221 | 0.6828 | 0.0000 | Al |
4 | 0.4553 | 0.1699 | 0.7132 | 0.0000 | Si |
5 | 0.1663 | 0.1451 | 0.3089 | 0.0000 | Si |
6 | 0.4934 | 0.2180 | 0.3356 | 0.0000 | Si |
7 | 0.0196 | 0.1996 | -0.1610 | 0.0000 | O |
8 | 0.5055 | -0.0166 | 0.7287 | 0.0000 | O |
9 | 0.2145 | 0.3091 | 0.2363 | 0.0000 | O |
10 | 0.1230 | 0.0227 | 0.1405 | 0.0000 | O |
11 | 0.3627 | 0.1455 | -0.2308 | 0.0000 | O |
12 | 0.4468 | 0.3329 | 0.1645 | 0.0000 | O |
13 | 0.2364 | 0.0352 | 0.4493 | 0.0000 | O |
14 | 0.3194 | 0.0028 | 0.1518 | 0.0000 | O |
15 | 0.2021 | 0.1040 | -0.1805 | 0.0000 | O |
16 | 0.4395 | 0.2285 | 0.4979 | 0.0000 | O |
17 | 0.0921 | 0.2209 | 0.4128 | 0.0000 | O |
18 | 0.3160 | 0.0020 | 0.2390 | 0.0000 | H |
19 | 0.3630 | -0.0250 | 0.1400 | 0.0000 | H |
20 | 0.1500 | 0.1160 | -0.2040 | 0.0000 | H |