N/N | x/a | y/b | z/c | B(j) | Occupancy |
---|---|---|---|---|---|
1 | 0.6565 | 0.7787 | 0.5923 | 0.8300 | Ce |
2 | 0.2181 | 0.7776 | 0.3103 | 1.0400 | Ce |
3 | 0.6100 | 0.9997 | 0.1947 | 0.1000 | Ti |
4 | 0.9610 | 0.8578 | 0.9115 | 0.3700 | Si |
5 | 0.0000 | 0.0000 | 0.5000 | 1.8200 | Na |
6 | 0.1405 | 0.4747 | 0.1748 | 2.0800 | Na |
7 | 0.5000 | 0.5000 | 0.5000 | 3.2600 | Na |
8 | 0.7914 | 0.3534 | 0.2433 | 1.2200 | C |
9 | 0.5993 | 0.6535 | 0.0623 | 0.7100 | C |
10 | 0.9335 | 0.7563 | 0.7068 | 0.6600 | O |
11 | 0.7925 | 0.9172 | 0.9089 | 0.8100 | O |
12 | 0.1613 | 0.9167 | 0.7245 | 0.7000 | O |
13 | 0.9563 | 0.8430 | 0.2243 | 0.8800 | O |
14 | 0.4053 | 0.9185 | 0.0677 | 0.8100 | O |
15 | 0.5504 | 0.9189 | 0.4993 | 0.7400 | O |
16 | 0.8735 | 0.3813 | 0.9915 | 0.0100 | O |
17 | 0.8096 | 0.4043 | 0.4623 | 2.4100 | O |
18 | 0.3343 | 0.3761 | 0.7702 | 1.4600 | O |
19 | 0.4046 | 0.3923 | 0.1771 | 1.3700 | O |
20 | 0.3076 | 0.7558 | 0.7489 | 1.2400 | O |
21 | 0.5458 | 0.7415 | 0.1339 | 0.9100 | O |