NN | Card | Specie | Formula | Space Group |
---|
1. | 1175 | [1], t-diopside, Mn | (Ca,Mn)(Mg,Mn)[Si2O6] | C 2/c |
2. | 1176 | [2], t-diopside | (Ca,Na)(Mg,Fe)Si2O6 | C 2/c |
3. | 1177 | [3], t-diopside | CaMgSi2O6 | C 2/c |
4. | 1178 | [4], t-diopside, at 24oC | CaMgSi2O6 | C 2/c |
5. | 1179 | [5], t-diopside, at 400oC | CaMgSi2O6 | C 2/c |
6. | 1180 | [6], t-diopside, at 700oC | CaMgSi2O6 | C 2/c |
7. | 1181 | [7], t-diopside, at 850oC | CaMgSi2O6 | C 2/c |
8. | 1182 | [8], t-diopside, at 1000oC | CaMgSi2O6 | C 2/c |
9. | 1183 | [9], t-diopside, at 1 atm | CaMgSi2O6 | C 2/c |
10. | 1184 | [10], t-diopside, at 23.6 kbar | CaMgSi2O6 | C 2/c |
11. | 1185 | [11], t-diopside, at 35.2 kbar | CaMgSi2O6 | C 2/c |
12. | 1186 | [12], t-diopside, at 45.5kbar | CaMgSi2O6 | C 2/c |
13. | 1187 | [13], t-diopside, at 53.0 kbar | CaMgSi2O6 | C 2/c |
14. | 1188 | [14], t-diopside, at 24oC | CaMgSi2O6 | C 2/c |
15. | 1189 | [15], t-diopside, at 800oC | CaMgSi2O6 | C 2/c |
16. | 1190 | [16], t-diopside, at 1000oC | CaMgSi2O6 | C 2/c |
17. | 1195 | [21], t-diopside, K, DF | Ca0.8K0.073Na0.023Mg0.95Fe0.06Cr0.07Al0.02Si2O6 | C 2/c |
18. | 1197 | [23], t-diopside, Fe, Al, syn | Ca[Mg0.55Fe0.34Al0.08][Si0.55Al0.42Fe0.03]O6 | C 2/c |
19. | 1200 | [26], t-diopside, syn, at 1330oC | CaMgSi2O6 | C 2/c |
20. | 1201 | [27], t-diopside, syn, at 1288oC | CaMg0.8Fe0.2Si2O6 | C 2/c |
21. | 1202 | [28], t-diopside, syn, at 1222oC | CaMg0.7Fe0.3Si2O6 | C 2/c |
22. | 1203 | [29], t-diopside, syn, at 1150oC | CaMg0.5Fe0.5Si2O6 | C 2/c |
23. | 1204 | [30], t-diopside, Fs(75)Wo(25) | (Ca,Fe)2Si2O6 | C 2/c |
24. | 1205 | [31], t-diopside, Fs(80)Wo(20) | (Ca,Fe)2Si2O6 | C 2/c |
25. | 1214 | [40], td-diopside, Di(80)En(20), at 130oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
26. | 1215 | [41], td-diopside, Di(80)En(20), at 25oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
27. | 1216 | [42], td-diopside, Di(80)En(20), at 400oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
28. | 1217 | [43], td-diopside, Di(80)En(20), at 700oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
29. | 5567 | [70], t-diopside, syn | [Ca0.75K0.23Mg0.02][Mg0.73Al0.27][Si1.97Al0.03]O6 | C 2/c |
30. | 5568 | [71], t-diopside, syn | [Ca0.9K0.07Mg0.03][Mg0.86Al0.14][Si1.94Al0.06]O6 | C 2/c |
31. | 6221 | [77], t-diopside, syn | CaMgSi2O6 | C 2/c |
32. | 6222 | [78], t-diopside, syn | CaMgSi2O6 | C 2/c |
33. | 6692 | [100], t-diopside, at 10oK | CaMgSi2O6 | C 2/c |
34. | 2892 | [102], t-diopside, at 1atm | CaMgSi2O6 | C 2/c |
35. | 3136 | [103], t-diopside, at 4.22GPa | CaMgSi2O6 | C 2/c |
36. | 3147 | [104], t-diopside, at 8.01GPa | CaMgSi2O6 | C 2/c |
37. | 3374 | [105], t-diopside, at 10.16GPa | CaMgSi2O6 | C 2/c |