List of specified cards with unique numbers under unique name

DIOPSIDE


NNCardSpecieFormulaSpace Group
1.    1175[1], t-diopside, Mn(Ca,Mn)(Mg,Mn)[Si2O6]C 2/c
2.    1176[2], t-diopside(Ca,Na)(Mg,Fe)Si2O6C 2/c
3.    1177[3], t-diopsideCaMgSi2O6C 2/c
4.    1178[4], t-diopside, at 24oCCaMgSi2O6C 2/c
5.    1179[5], t-diopside, at 400oCCaMgSi2O6C 2/c
6.    1180[6], t-diopside, at 700oCCaMgSi2O6C 2/c
7.    1181[7], t-diopside, at 850oCCaMgSi2O6C 2/c
8.    1182[8], t-diopside, at 1000oCCaMgSi2O6C 2/c
9.    1183[9], t-diopside, at 1 atmCaMgSi2O6C 2/c
10.    1184[10], t-diopside, at 23.6 kbarCaMgSi2O6C 2/c
11.    1185[11], t-diopside, at 35.2 kbarCaMgSi2O6C 2/c
12.    1186[12], t-diopside, at 45.5kbarCaMgSi2O6C 2/c
13.    1187[13], t-diopside, at 53.0 kbarCaMgSi2O6C 2/c
14.    1188[14], t-diopside, at 24oCCaMgSi2O6C 2/c
15.    1189[15], t-diopside, at 800oCCaMgSi2O6C 2/c
16.    1190[16], t-diopside, at 1000oCCaMgSi2O6C 2/c
17.    1191[17], t-diopside, analogueNaFeGe2O6C 2/c
18.    1192[18], alpha, t-diopside, analogueNa2V2O6C 2/c
19.    1193[19], t-diopside, analogue, DF[Ca0.97Co0.03][Mg0.831Co0.169]Si2O6C 2/c
20.    1194[20], t-diopside, analogue, DF[Ca0.95Co0.05][Mg0.486Co0.514]Si2O6C 2/c
21.    1195[21], t-diopside, K, DFCa0.8K0.073Na0.023Mg0.95Fe0.06Cr0.07Al0.02Si2O6C 2/c
22.    1196[22], t-diopside, analogueCd2Ge2O6B 2/b
23.    1197[23], t-diopside, Fe, Al, synCa[Mg0.55Fe0.34Al0.08][Si0.55Al0.42Fe0.03]O6C 2/c
24.    1198[24], t-diopside, Ni-analogueCaNiSi2O6C 2/c
25.    1199[25], t-diopside, Co-analogueCaCoSi2O6C 2/c
26.    1200[26], t-diopside, syn, at 1330oCCaMgSi2O6C 2/c
27.    1201[27], t-diopside, syn, at 1288oCCaMg0.8Fe0.2Si2O6C 2/c
28.    1202[28], t-diopside, syn, at 1222oCCaMg0.7Fe0.3Si2O6C 2/c
29.    1203[29], t-diopside, syn, at 1150oCCaMg0.5Fe0.5Si2O6C 2/c
30.    1204[30], t-diopside, Fs(75)Wo(25)(Ca,Fe)2Si2O6C 2/c
31.    1205[31], t-diopside, Fs(80)Wo(20)(Ca,Fe)2Si2O6C 2/c
32.    1206[32], t-diopside, analogueKInGe2O6C 2/c
33.    1207[33], t-diopside, In-analogue, at 1770oK + 6 GPaNaInSi2O6C 2/c
34.    1208[34], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPaNaIn0.8Sc0.2Si2O6C 2/c
35.    1209[35], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPaNaIn0.65Sc0.35Si2O6C 2/c
36.    1210[36], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPaNaIn0.6Sc0.4Si2O6C 2/c
37.    1211[37], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPaNaIn0.5Sc0.5Si2O6C 2/c
38.    1212[38], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPaNaIn0.4Sc0.6Si2O6C 2/c
39.    1213[39], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPaNaIn0.2Sc0.8Si2O6C 2/c
40.    1214[40], td-diopside, Di(80)En(20), at 130oC, DFCa0.8Mg1.2Si2O6C 2/c
41.    1215[41], td-diopside, Di(80)En(20), at 25oC, DFCa0.8Mg1.2Si2O6C 2/c
42.    1216[42], td-diopside, Di(80)En(20), at 400oC, DFCa0.8Mg1.2Si2O6C 2/c
43.    1217[43], td-diopside, Di(80)En(20), at 700oC, DFCa0.8Mg1.2Si2O6C 2/c
44.    1218[44], t-diopside, analogueMgGeO3C 2/c
45.    1219[45], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
46.    1220[46], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
47.    1221[47], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
48.    1222[48], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
49.    1223[49], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
50.    1224[50], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
51.    1225[51], t-diopside, analogue(Na,Ca)(Sc,Zn)Si2O6C 2/c
52.    1226[52], t-diopside, analogue(Li,Na)GaSi2O6C 2/c
53.    1227[53], t-diopside, analogue(Li,Na)GaSi2O6C 2/c
54.    1228[54], t-diopside, analogue(Li,Na)GaSi2O6C 2/c
55.    1229[55], t-diopside, analogue(Li,Na)GaSi2O6C 2/c
56.    1230[56], t-diopside, analogue(Li,Na)GaSi2O6C 2/c
57.    1231[57], t-diopside, analogue, at 1770oK+6 GPaLiGaSi2O6C 2/c
58.    1232[58], t-diopside, analogue, at 1073oK+1 atmLiGaSi2O6C 2/c
59.    1233[59], t-diopside, analogue, at 1123oK+1 atmLiGaSi2O6C 2/c
60.    1234[60], t-diopside, Di(70)CaTs(30), analogue, at 25oCCa[Mg0.7Al0.3][Si1.7Al0.3]O6C 2/c
61.    1235[61], t-diopside, Di(70)CaTs(30), analogue, at 300oCCa[Mg0.7Al0.3][Si1.7Al0.3]O6C 2/c
62.    1236[62], t-diopside, Di(70)CaTs(30), analogue, at 500oCCa[Mg0.7Al0.3][Si1.7Al0.3]O6C 2/c
63.    1237[63], t-diopside, Di(70)CaTs(30), analogue, at 700oCCa[Mg0.7Al0.3][Si1.7Al0.3]O6C 2/c
64.    1238[64], t-diopside, Di(50)CaTs(50), analogue, at 700oCCa[Mg0.5Al0.5][Si1.5Al0.5]O6C 2/c
65.    1239[65], t-diopside, at 0 GPa, analogueFeGeO3C 2/c
66.    1240[66], t-diopside, at 1.5 GPa, analogueFeGeO3C 2/c
67.    1241[67], t-diopside, at 4.5 GPa, analogueFeGeO3C 2/c
68.    1242[68], t-diopside, at 7.4 GPa, analogueFeGeO3C 2/c
69.    1243[69], t-diopside, at 8.2 GPa, analogueFeGeO3C 2/c
70.    5567[70], t-diopside, syn[Ca0.75K0.23Mg0.02][Mg0.73Al0.27][Si1.97Al0.03]O6C 2/c
71.    5568[71], t-diopside, syn[Ca0.9K0.07Mg0.03][Mg0.86Al0.14][Si1.94Al0.06]O6C 2/c
72.    6216[72], t-diopside, analogue(Ca,Na)(Mg,Ti3+,Ti4+)Si2O6C 2/c
73.    6217[73], t-diopside, analogue(Ca,Na)(Mg,Ti3+,Ti4+)Si2O6C 2/c
74.    6218[74], t-diopside, analogue(Ca,Na)(Mg,Ti3+,Ti4+)Si2O6C 2/c
75.    6219[75], t-diopside, analogue(Ca,Na)(Mg,Ti3+,Ti4+)Si2O6C 2/c
76.    6220[76], t-diopside, analogue(Ca,Na)(Mg,Ti3+,Ti4+)Si2O6C 2/c
77.    6221[77], t-diopside, synCaMgSi2O6C 2/c
78.    6222[78], t-diopside, synCaMgSi2O6C 2/c
79.    6223[79], t-diopside, Fe-analogueCa(Mg,Fe)Si2O6C 2/c
80.    6224[80], t-diopside, Fe-analogueCa(Mg,Fe)(Si,Fe)2O6C 2/c
81.    6225[81], t-diopside, Fe-analogueCa(Mg,Fe)(Si,Fe)2O6C 2/c
82.    6226[82], t-diopside, Fe-analogueCa(Mg,Fe)(Si,Fe)2O6C 2/c
83.    6227[83], t-diopside, Fe-analogueCa(Mg,Fe)(Si,Fe)2O6C 2/c
84.    3879[85], t-diopside, Li-Sc, analogueLiScSi2O6C 2/c
85.    3880[86], t-diopside, Ni, analogueCaNi0.8Mg0.2Si2O6C 2/c
86.    3881[87], t-diopside, Ni, analogueCaNi0.5Mg0.5Si2O6C 2/c
87.    3882[88], t-diopside, Ni, analogueCaNi0.25Mg0.75Si2O6C 2/c
88.    3883[89], t-diopside, Ni, analogueCaNiSi2O6C 2/c
89.    3885[90], t-diopside, Na, In, analogueNaInSi2O6C 2/c
90.    3876[91], t-diopside, Na- Sc- analogueNaScSi2O6C 2/c
91.    3886[92], t-diopside, analogue, at 1673oK,Ca0.742Fe0.1Mg0.016Al1.384Si1.534O6C 2/c
92.    5736[93], t-diopside, analogue[Ca0.61Fe0.13K0.17(Mg,Mn,Na)0.1][Al0.61(Mg0.39]Al0.39Si1.61O6C 2/c
93.    6367[94], t-diopside, analogueCaZnSi2O6C 2/c
94.    6368[95], t-diopside, analogueCaZnGe2O6C 2/c
95.    6688[96], t-diopside, analogue, at 25oC[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6C 2/c
96.    6689[97], t-diopside, analogue, at 200oC[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6C 2/c
97.    6690[98], t-diopside, analogue, at 400oC[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6C 2/c
98.    6691[99], t-diopside, analogue, at 620oC[Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6C 2/c
99.    6692[100], t-diopside, at 10oKCaMgSi2O6C 2/c
100.    6693[101], t-diopside, analogue[Ca0.36Na0.56Mg0.08][Mg0.73Si0.27]Si2O6C 2/c
101.    2892[102], t-diopside, at 1atmCaMgSi2O6C 2/c
102.    3136[103], t-diopside, at 4.22GPaCaMgSi2O6C 2/c
103.    3147[104], t-diopside, at 8.01GPaCaMgSi2O6C 2/c
104.    3374[105], t-diopside, at 10.16GPaCaMgSi2O6C 2/c
105.    7894[106], t-diopside, analogue, at 4oKCoGeO3C 2/c
106.    7895[107], t-diopside, analogue, at 50oKCoGeO3C 2/c
107.    7896[108], t-diopside, analogue, at 298oKCoGeO3C 2/c
108.    7897[109], t-diopside, analogue, at 303oKLiGaSi2O6C 2/c
109.    7898[110], t-diopside, analogue, at 673oKLiGaSi2O6C 2/c
110.    7899[111], t-diopside, analogue, at 1073oKLiGaSi2O6C 2/c
111.    8447[112], t-diopside[Ca0.8Fe0.2][Mg0.8Fe0.2]Si2O6C 2/c