NN | Карта | Спецификация | Формула | Uпот | Ионная сила |
---|
1. | 1897 | [1], t-diopside, at 24oC | CaFeSi2O6 | 32174 | 32 |
2. | 1898 | [2], t-diopside, at 400oC | CaFeSi2O6 | 32071 | 32 |
3. | 1899 | [3], t-diopside, at 600oC | CaFeSi2O6 | 32010 | 32 |
4. | 1900 | [4], t-diopside, at 800oC | CaFeSi2O6 | 31956 | 32 |
5. | 1901 | [5], t-diopside, at 900oC | CaFeSi2O6 | 31911 | 32 |
6. | 1902 | [6], t-diopside, at 1000oC | CaFeSi2O6 | 31880 | 32 |
7. | 1903 | [7], t-diopside, Mn | CaFe0.68Mn0.38Si2O6 | 32106 | 32 |
8. | 1904 | [8], t-diopside, syn, at 0.1 MPa | CaFeSi2O6 | 32192 | 32 |
9. | 1905 | [9], t-diopside, syn, at 1.1 GPa | CaFeSi2O6 | 32299 | 32 |
10. | 1884 | [10], t-diopside, syn, at 2.1 GPa | CaFeSi2O6 | 32372 | 32 |
11. | 1885 | [11], t-diopside, syn, at 2.8 GPa | CaFeSi2O6 | 32442 | 32 |
12. | 1886 | [12], t-diopside, syn, at 3.6 GPa | CaFeSi2O6 | 32504 | 32 |
13. | 1887 | [13], t-diopside, syn, at 4.2 GPa | CaFeSi2O6 | 32579 | 32 |
14. | 1888 | [14], t-diopside, syn, at 4.6 GPa | CaFeSi2O6 | 32608 | 32 |
15. | 1889 | [15], t-diopside, syn, at 5.3 GPa | CaFeSi2O6 | 32640 | 32 |
16. | 1890 | [16], t-diopside, syn, at 6.3 GPa | CaFeSi2O6 | 32723 | 32 |
17. | 1891 | [17], t-diopside, syn, at 7.6 GPa | CaFeSi2O6 | 32824 | 32 |
18. | 1892 | [18], t-diopside, syn, at 8.7 GPa | CaFeSi2O6 | 32907 | 32 |
19. | 1893 | [19], t-diopside, syn, at 9.9 GPa | CaFeSi2O6 | 32992 | 32 |
20. | 1894 | [20], t-diopside, syn | Ca[Fe2+0.98Fe3+0.02]Si2O6 | 32161 | 32 |
21. | 1895 | [21], t-diopside, syn, at 1120oC | CaMg0.3Fe0.7Si2O6 | 32254 | 32 |