NN | Карточка | Спецификация | Формула | Пространственная группа |
---|
1. | 1177 | [3], t-diopside | CaMgSi2O6 | C 2/c |
2. | 1178 | [4], t-diopside, at 24oC | CaMgSi2O6 | C 2/c |
3. | 1179 | [5], t-diopside, at 400oC | CaMgSi2O6 | C 2/c |
4. | 1180 | [6], t-diopside, at 700oC | CaMgSi2O6 | C 2/c |
5. | 1181 | [7], t-diopside, at 850oC | CaMgSi2O6 | C 2/c |
6. | 1182 | [8], t-diopside, at 1000oC | CaMgSi2O6 | C 2/c |
7. | 1183 | [9], t-diopside, at 1 atm | CaMgSi2O6 | C 2/c |
8. | 1184 | [10], t-diopside, at 23.6 kbar | CaMgSi2O6 | C 2/c |
9. | 1185 | [11], t-diopside, at 35.2 kbar | CaMgSi2O6 | C 2/c |
10. | 1186 | [12], t-diopside, at 45.5kbar | CaMgSi2O6 | C 2/c |
11. | 1187 | [13], t-diopside, at 53.0 kbar | CaMgSi2O6 | C 2/c |
12. | 1188 | [14], t-diopside, at 24oC | CaMgSi2O6 | C 2/c |
13. | 1189 | [15], t-diopside, at 800oC | CaMgSi2O6 | C 2/c |
14. | 1190 | [16], t-diopside, at 1000oC | CaMgSi2O6 | C 2/c |
15. | 1200 | [26], t-diopside, syn, at 1330oC | CaMgSi2O6 | C 2/c |
16. | 1201 | [27], t-diopside, syn, at 1288oC | CaMg0.8Fe0.2Si2O6 | C 2/c |
17. | 1202 | [28], t-diopside, syn, at 1222oC | CaMg0.7Fe0.3Si2O6 | C 2/c |
18. | 1203 | [29], t-diopside, syn, at 1150oC | CaMg0.5Fe0.5Si2O6 | C 2/c |
19. | 6221 | [77], t-diopside, syn | CaMgSi2O6 | C 2/c |
20. | 6222 | [78], t-diopside, syn | CaMgSi2O6 | C 2/c |
21. | 6692 | [100], t-diopside, at 10oK | CaMgSi2O6 | C 2/c |
22. | 2892 | [102], t-diopside, at 1atm | CaMgSi2O6 | C 2/c |
23. | 3136 | [103], t-diopside, at 4.22GPa | CaMgSi2O6 | C 2/c |
24. | 3147 | [104], t-diopside, at 8.01GPa | CaMgSi2O6 | C 2/c |
25. | 3374 | [105], t-diopside, at 10.16GPa | CaMgSi2O6 | C 2/c |