NN | Карточка | Спецификация | Формула | Пространственная группа |
---|
1. | 1175 | [1], t-diopside, Mn | (Ca,Mn)(Mg,Mn)[Si2O6] | C 2/c |
2. | 1176 | [2], t-diopside | (Ca,Na)(Mg,Fe)Si2O6 | C 2/c |
3. | 1177 | [3], t-diopside | CaMgSi2O6 | C 2/c |
4. | 1178 | [4], t-diopside, at 24oC | CaMgSi2O6 | C 2/c |
5. | 1179 | [5], t-diopside, at 400oC | CaMgSi2O6 | C 2/c |
6. | 1180 | [6], t-diopside, at 700oC | CaMgSi2O6 | C 2/c |
7. | 1181 | [7], t-diopside, at 850oC | CaMgSi2O6 | C 2/c |
8. | 1182 | [8], t-diopside, at 1000oC | CaMgSi2O6 | C 2/c |
9. | 1183 | [9], t-diopside, at 1 atm | CaMgSi2O6 | C 2/c |
10. | 1184 | [10], t-diopside, at 23.6 kbar | CaMgSi2O6 | C 2/c |
11. | 1185 | [11], t-diopside, at 35.2 kbar | CaMgSi2O6 | C 2/c |
12. | 1186 | [12], t-diopside, at 45.5kbar | CaMgSi2O6 | C 2/c |
13. | 1187 | [13], t-diopside, at 53.0 kbar | CaMgSi2O6 | C 2/c |
14. | 1188 | [14], t-diopside, at 24oC | CaMgSi2O6 | C 2/c |
15. | 1189 | [15], t-diopside, at 800oC | CaMgSi2O6 | C 2/c |
16. | 1190 | [16], t-diopside, at 1000oC | CaMgSi2O6 | C 2/c |
17. | 1191 | [17], t-diopside, analogue | NaFeGe2O6 | C 2/c |
18. | 1192 | [18], alpha, t-diopside, analogue | Na2V2O6 | C 2/c |
19. | 1193 | [19], t-diopside, analogue, DF | [Ca0.97Co0.03][Mg0.831Co0.169]Si2O6 | C 2/c |
20. | 1194 | [20], t-diopside, analogue, DF | [Ca0.95Co0.05][Mg0.486Co0.514]Si2O6 | C 2/c |
21. | 1195 | [21], t-diopside, K, DF | Ca0.8K0.073Na0.023Mg0.95Fe0.06Cr0.07Al0.02Si2O6 | C 2/c |
22. | 1196 | [22], t-diopside, analogue | Cd2Ge2O6 | B 2/b |
23. | 1197 | [23], t-diopside, Fe, Al, syn | Ca[Mg0.55Fe0.34Al0.08][Si0.55Al0.42Fe0.03]O6 | C 2/c |
24. | 1198 | [24], t-diopside, Ni-analogue | CaNiSi2O6 | C 2/c |
25. | 1199 | [25], t-diopside, Co-analogue | CaCoSi2O6 | C 2/c |
26. | 1200 | [26], t-diopside, syn, at 1330oC | CaMgSi2O6 | C 2/c |
27. | 1201 | [27], t-diopside, syn, at 1288oC | CaMg0.8Fe0.2Si2O6 | C 2/c |
28. | 1202 | [28], t-diopside, syn, at 1222oC | CaMg0.7Fe0.3Si2O6 | C 2/c |
29. | 1203 | [29], t-diopside, syn, at 1150oC | CaMg0.5Fe0.5Si2O6 | C 2/c |
30. | 1204 | [30], t-diopside, Fs(75)Wo(25) | (Ca,Fe)2Si2O6 | C 2/c |
31. | 1205 | [31], t-diopside, Fs(80)Wo(20) | (Ca,Fe)2Si2O6 | C 2/c |
32. | 1206 | [32], t-diopside, analogue | KInGe2O6 | C 2/c |
33. | 1207 | [33], t-diopside, In-analogue, at 1770oK + 6 GPa | NaInSi2O6 | C 2/c |
34. | 1208 | [34], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa | NaIn0.8Sc0.2Si2O6 | C 2/c |
35. | 1209 | [35], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa | NaIn0.65Sc0.35Si2O6 | C 2/c |
36. | 1210 | [36], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa | NaIn0.6Sc0.4Si2O6 | C 2/c |
37. | 1211 | [37], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa | NaIn0.5Sc0.5Si2O6 | C 2/c |
38. | 1212 | [38], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa | NaIn0.4Sc0.6Si2O6 | C 2/c |
39. | 1213 | [39], t-diopside, In, Sc-analogue, at 1770oK+ 6 GPa | NaIn0.2Sc0.8Si2O6 | C 2/c |
40. | 1214 | [40], td-diopside, Di(80)En(20), at 130oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
41. | 1215 | [41], td-diopside, Di(80)En(20), at 25oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
42. | 1216 | [42], td-diopside, Di(80)En(20), at 400oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
43. | 1217 | [43], td-diopside, Di(80)En(20), at 700oC, DF | Ca0.8Mg1.2Si2O6 | C 2/c |
44. | 1218 | [44], t-diopside, analogue | MgGeO3 | C 2/c |
45. | 1219 | [45], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
46. | 1220 | [46], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
47. | 1221 | [47], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
48. | 1222 | [48], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
49. | 1223 | [49], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
50. | 1224 | [50], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
51. | 1225 | [51], t-diopside, analogue | (Na,Ca)(Sc,Zn)Si2O6 | C 2/c |
52. | 1226 | [52], t-diopside, analogue | (Li,Na)GaSi2O6 | C 2/c |
53. | 1227 | [53], t-diopside, analogue | (Li,Na)GaSi2O6 | C 2/c |
54. | 1228 | [54], t-diopside, analogue | (Li,Na)GaSi2O6 | C 2/c |
55. | 1229 | [55], t-diopside, analogue | (Li,Na)GaSi2O6 | C 2/c |
56. | 1230 | [56], t-diopside, analogue | (Li,Na)GaSi2O6 | C 2/c |
57. | 1231 | [57], t-diopside, analogue, at 1770oK+6 GPa | LiGaSi2O6 | C 2/c |
58. | 1232 | [58], t-diopside, analogue, at 1073oK+1 atm | LiGaSi2O6 | C 2/c |
59. | 1233 | [59], t-diopside, analogue, at 1123oK+1 atm | LiGaSi2O6 | C 2/c |
60. | 1234 | [60], t-diopside, Di(70)CaTs(30), analogue, at 25oC | Ca[Mg0.7Al0.3][Si1.7Al0.3]O6 | C 2/c |
61. | 1235 | [61], t-diopside, Di(70)CaTs(30), analogue, at 300oC | Ca[Mg0.7Al0.3][Si1.7Al0.3]O6 | C 2/c |
62. | 1236 | [62], t-diopside, Di(70)CaTs(30), analogue, at 500oC | Ca[Mg0.7Al0.3][Si1.7Al0.3]O6 | C 2/c |
63. | 1237 | [63], t-diopside, Di(70)CaTs(30), analogue, at 700oC | Ca[Mg0.7Al0.3][Si1.7Al0.3]O6 | C 2/c |
64. | 1238 | [64], t-diopside, Di(50)CaTs(50), analogue, at 700oC | Ca[Mg0.5Al0.5][Si1.5Al0.5]O6 | C 2/c |
65. | 1239 | [65], t-diopside, at 0 GPa, analogue | FeGeO3 | C 2/c |
66. | 1240 | [66], t-diopside, at 1.5 GPa, analogue | FeGeO3 | C 2/c |
67. | 1241 | [67], t-diopside, at 4.5 GPa, analogue | FeGeO3 | C 2/c |
68. | 1242 | [68], t-diopside, at 7.4 GPa, analogue | FeGeO3 | C 2/c |
69. | 1243 | [69], t-diopside, at 8.2 GPa, analogue | FeGeO3 | C 2/c |
70. | 5567 | [70], t-diopside, syn | [Ca0.75K0.23Mg0.02][Mg0.73Al0.27][Si1.97Al0.03]O6 | C 2/c |
71. | 5568 | [71], t-diopside, syn | [Ca0.9K0.07Mg0.03][Mg0.86Al0.14][Si1.94Al0.06]O6 | C 2/c |
72. | 6216 | [72], t-diopside, analogue | (Ca,Na)(Mg,Ti3+,Ti4+)Si2O6 | C 2/c |
73. | 6217 | [73], t-diopside, analogue | (Ca,Na)(Mg,Ti3+,Ti4+)Si2O6 | C 2/c |
74. | 6218 | [74], t-diopside, analogue | (Ca,Na)(Mg,Ti3+,Ti4+)Si2O6 | C 2/c |
75. | 6219 | [75], t-diopside, analogue | (Ca,Na)(Mg,Ti3+,Ti4+)Si2O6 | C 2/c |
76. | 6220 | [76], t-diopside, analogue | (Ca,Na)(Mg,Ti3+,Ti4+)Si2O6 | C 2/c |
77. | 6221 | [77], t-diopside, syn | CaMgSi2O6 | C 2/c |
78. | 6222 | [78], t-diopside, syn | CaMgSi2O6 | C 2/c |
79. | 6223 | [79], t-diopside, Fe-analogue | Ca(Mg,Fe)Si2O6 | C 2/c |
80. | 6224 | [80], t-diopside, Fe-analogue | Ca(Mg,Fe)(Si,Fe)2O6 | C 2/c |
81. | 6225 | [81], t-diopside, Fe-analogue | Ca(Mg,Fe)(Si,Fe)2O6 | C 2/c |
82. | 6226 | [82], t-diopside, Fe-analogue | Ca(Mg,Fe)(Si,Fe)2O6 | C 2/c |
83. | 6227 | [83], t-diopside, Fe-analogue | Ca(Mg,Fe)(Si,Fe)2O6 | C 2/c |
84. | 3879 | [85], t-diopside, Li-Sc, analogue | LiScSi2O6 | C 2/c |
85. | 3880 | [86], t-diopside, Ni, analogue | CaNi0.8Mg0.2Si2O6 | C 2/c |
86. | 3881 | [87], t-diopside, Ni, analogue | CaNi0.5Mg0.5Si2O6 | C 2/c |
87. | 3882 | [88], t-diopside, Ni, analogue | CaNi0.25Mg0.75Si2O6 | C 2/c |
88. | 3883 | [89], t-diopside, Ni, analogue | CaNiSi2O6 | C 2/c |
89. | 3885 | [90], t-diopside, Na, In, analogue | NaInSi2O6 | C 2/c |
90. | 3876 | [91], t-diopside, Na- Sc- analogue | NaScSi2O6 | C 2/c |
91. | 3886 | [92], t-diopside, analogue, at 1673oK, | Ca0.742Fe0.1Mg0.016Al1.384Si1.534O6 | C 2/c |
92. | 5736 | [93], t-diopside, analogue | [Ca0.61Fe0.13K0.17(Mg,Mn,Na)0.1][Al0.61(Mg0.39]Al0.39Si1.61O6 | C 2/c |
93. | 6367 | [94], t-diopside, analogue | CaZnSi2O6 | C 2/c |
94. | 6368 | [95], t-diopside, analogue | CaZnGe2O6 | C 2/c |
95. | 6688 | [96], t-diopside, analogue, at 25oC | [Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6 | C 2/c |
96. | 6689 | [97], t-diopside, analogue, at 200oC | [Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6 | C 2/c |
97. | 6690 | [98], t-diopside, analogue, at 400oC | [Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6 | C 2/c |
98. | 6691 | [99], t-diopside, analogue, at 620oC | [Na0.5Ca0.5][Cr3+0.5Mg0.5]Si2O6 | C 2/c |
99. | 6692 | [100], t-diopside, at 10oK | CaMgSi2O6 | C 2/c |
100. | 6693 | [101], t-diopside, analogue | [Ca0.36Na0.56Mg0.08][Mg0.73Si0.27]Si2O6 | C 2/c |
101. | 2892 | [102], t-diopside, at 1atm | CaMgSi2O6 | C 2/c |
102. | 3136 | [103], t-diopside, at 4.22GPa | CaMgSi2O6 | C 2/c |
103. | 3147 | [104], t-diopside, at 8.01GPa | CaMgSi2O6 | C 2/c |
104. | 3374 | [105], t-diopside, at 10.16GPa | CaMgSi2O6 | C 2/c |
105. | 7894 | [106], t-diopside, analogue, at 4oK | CoGeO3 | C 2/c |
106. | 7895 | [107], t-diopside, analogue, at 50oK | CoGeO3 | C 2/c |
107. | 7896 | [108], t-diopside, analogue, at 298oK | CoGeO3 | C 2/c |
108. | 7897 | [109], t-diopside, analogue, at 303oK | LiGaSi2O6 | C 2/c |
109. | 7898 | [110], t-diopside, analogue, at 673oK | LiGaSi2O6 | C 2/c |
110. | 7899 | [111], t-diopside, analogue, at 1073oK | LiGaSi2O6 | C 2/c |
111. | 8447 | [112], t-diopside | [Ca0.8Fe0.2][Mg0.8Fe0.2]Si2O6 | C 2/c |