NN | Карточка | Спецификация | Формула | Пространственная группа |
---|
1. | 1065 | [1], t-cristobalite-alpha, low, at 28oC | SiO2 | P 4(1)2(1)2 |
2. | 1066 | [2], t-cristobalite-alpha, low, at 65oC | SiO2 | P 4(1)2(1)2 |
3. | 1067 | [3], t-cristobalite-alpha, low, at 103oC | SiO2 | P 4(1)2(1)2 |
4. | 1068 | [4], t-cristobalite-alpha, low, at 142oC | SiO2 | P 4(1)2(1)2 |
5. | 1069 | [5], t-cristobalite-alpha, low, at 179oC | SiO2 | P 4(1)2(1)2 |
6. | 1070 | [6], t-cristobalite-alpha, low, at 210oC | SiO2 | P 4(1)2(1)2 |
7. | 1071 | [7], t-cristobalite-alpha, low, at 230oC | SiO2 | P 4(1)2(1)2 |
8. | 1072 | [8], t-cristobalite-beta, high, at 221oC, DF | SiO2 | *F d3m |
9. | 1073 | [9], t-cristobalite-beta, high, at 248oC, DF | SiO2 | *F d3m |
10. | 1051 | [10], t-cristobalite-beta, high, at 273oC, DF | SiO2 | *F d3m |
11. | 1052 | [11], t-cristobalite-beta, high, at 310oC | SiO2 | *F d3m |
12. | 1053 | [12], t-cristobalite-alpha, at 0.01GPa+298oK | SiO2 | P 4(1)2(1)2 |
13. | 1054 | [13], t-cristobalite-alpha, at 0.2GPa+298oK | SiO2 | P 4(1)2(1)2 |
14. | 1055 | [14], t-cristobalite-alpha, at 0.4GPa+298oK | SiO2 | P 4(1)2(1)2 |
15. | 1056 | [15], t-cristobalite-alpha, at 0.6GPa+298oK | SiO2 | P 4(1)2(1)2 |
16. | 1057 | [16], t-cristobalite-alpha, at0.6GPa+ 60oK | SiO2 | P 4(1)2(1)2 |
17. | 1059 | [18], t-cristobalite-alpha, at 0.2GPa+ 60oK | SiO2 | P 4(1)2(1)2 |
18. | 1060 | [19], t-cristobalite-alpha, at 0.01GPa+ 60oK | SiO2 | P 4(1)2(1)2 |
19. | 8140 | [24], t-cristobalite-alpha, at 0.2 GPa | SiO2 | P 4(1)2(1)2 |
20. | 8141 | [25], t-cristobalite-alpha, at 3.6 GPa | SiO2 | P 4(1)2(1)2 |
21. | 8142 | [26], t-cristobalite-alpha, at 5.4 GPa | SiO2 | P 4(1)2(1)2 |
22. | 8143 | [27], t-cristobalite-alpha, at 7.3 GPa | SiO2 | P 4(1)2(1)2 |
23. | 8144 | [28], t-cristobalite-alpha, at 9.1 GPa | SiO2 | P 4(1)2(1)2 |
24. | 8145 | [29], td-cristobalite-alpha, at 4.9 GPa | SiO2 | P 2(1)/c |
25. | 8146 | [30], td-cristobalite-alpha, at 7.4 GPa | SiO2 | P 2(1)/c |