Список специфицированных карточек с уникальными номерами под уникальным названием

CRISTOBALITE


NNКарточкаСпецификацияФормулаПространственная группа
1.1065[1], t-cristobalite-alpha, low, at 28oCSiO2P 4(1)2(1)2
2.1066[2], t-cristobalite-alpha, low, at 65oCSiO2P 4(1)2(1)2
3.1067[3], t-cristobalite-alpha, low, at 103oCSiO2P 4(1)2(1)2
4.1068[4], t-cristobalite-alpha, low, at 142oCSiO2P 4(1)2(1)2
5.1069[5], t-cristobalite-alpha, low, at 179oCSiO2P 4(1)2(1)2
6.1070[6], t-cristobalite-alpha, low, at 210oCSiO2P 4(1)2(1)2
7.1071[7], t-cristobalite-alpha, low, at 230oCSiO2P 4(1)2(1)2
8.1072[8], t-cristobalite-beta, high, at 221oC, DFSiO2*F d3m
9.1073[9], t-cristobalite-beta, high, at 248oC, DFSiO2*F d3m
10.1051[10], t-cristobalite-beta, high, at 273oC, DFSiO2*F d3m
11.1052[11], t-cristobalite-beta, high, at 310oCSiO2*F d3m
12.1053[12], t-cristobalite-alpha, at 0.01GPa+298oKSiO2P 4(1)2(1)2
13.1054[13], t-cristobalite-alpha, at 0.2GPa+298oKSiO2P 4(1)2(1)2
14.1055[14], t-cristobalite-alpha, at 0.4GPa+298oKSiO2P 4(1)2(1)2
15.1056[15], t-cristobalite-alpha, at 0.6GPa+298oKSiO2P 4(1)2(1)2
16.1057[16], t-cristobalite-alpha, at0.6GPa+ 60oKSiO2P 4(1)2(1)2
17.1058[17], t-cristobalite-alpha, at 0.4GPa+ 60oKSiO2P 4(1)2(1)2
18.1059[18], t-cristobalite-alpha, at 0.2GPa+ 60oKSiO2P 4(1)2(1)2
19.1060[19], t-cristobalite-alpha, at 0.01GPa+ 60oKSiO2P 4(1)2(1)2
20.1061[20], t-cristobalite-alpha, analogueNa1.95Al1.95Si0.05O4P 4(1)2(1)2
21.1062[21], td-cristobalite-alpha, analogue, DFNa1.75Al1.75Si0.25O4P bca
22.1063[22], t-cristobalite-alpha, analogueNa1.65Al1.65Si0.35O4P 4(1)2(1)2
23.1064[23], td-cristobalite-alpha, analogue, DFNa1.55Al1.55Si0.45O4P bca
24.8140[24], t-cristobalite-alpha, at 0.2 GPaSiO2P 4(1)2(1)2
25.8141[25], t-cristobalite-alpha, at 3.6 GPaSiO2P 4(1)2(1)2
26.8142[26], t-cristobalite-alpha, at 5.4 GPaSiO2P 4(1)2(1)2
27.8143[27], t-cristobalite-alpha, at 7.3 GPaSiO2P 4(1)2(1)2
28.8144[28], t-cristobalite-alpha, at 9.1 GPaSiO2P 4(1)2(1)2
29.8145[29], td-cristobalite-alpha, at 4.9 GPaSiO2P 2(1)/c
30.8146[30], td-cristobalite-alpha, at 7.4 GPaSiO2P 2(1)/c
31.8147[31], td-cristobalite-alpha, at 10.1 GPaSiO2P 2(1)/c
32.10934[32], t-cristobalite-alphaSiO2P 4(1)2(1)2